"ML-A" Film
White film for wood profiles in exterior environments ML-A is an ideal exterior grade film. Like rigid PVC siding, it can be formulated in white and selected light colors only. It has good hot and cold weather properties, excellent long lasting color hold, and surface integrity under a constant barrage of sunlight. ML-A film can also be painted when custom colors are desired. In addition, ML-A film is resistant to non-abrasive household cleansers in dilute form such as ammonia water, aliphatic benzene and rubbing alcohol. MLA laminate is ideal over finger-jointed boards, plywood components and other rough substrates since it successfully hides minor surface imperfections. MLA can be embossed with woodgrain, stipple and smooth textures as required. | Article Group: | 6524 ML-A | | Color: | Opaque variations in range of white only | | Embossing: | 083, 055 or custom emboss to requirements | | Film Structure: | one-ply opaque film |
| PROPERTIES | STANDARD TEST METHOD | TYPICAL VALUES | | Thickness | DIN 53353 | 200 µm ± 10% | | Tensile Strength | DIN 53455 | MD: ≥20 N/mm²
CD: ≥8 N/mm² | | Elongation at break | DIN 53455 | MD: ≤100%
CD: ≤100% | | Abrasion resistance | DIN 54021/54002 | Grade 5 | | Scratch resistance | Erichsentester 435 | ≤20 cN | | Embossing stability | RENOLIT | ≥80°C | | Shrinkage (10 min, 60°C) | DIN 53377 | ≤2.5% | | Permanent temperature resistance | RENOLIT | ≥65°C | | Weatherability | DIN 53387 | Permitted total irradiation ≤14.5 GJ/m² (Xenontest 450) grade 3 on the gray-scale
(DIN EN 20105 A 02) | | Chemical resistance | N/A | Resistant to normal household cleansing agents e.g Ammonia water, aliphatic benzene, rubbing alcohol, cleansing-agents (non-abrasive), building materials e.g. cement, gypsum . Not resistant to organic solvents (e.g. varnish thinners or removers, polish, etc.) | | Maintenance | N/A | Appropriate cleaning with standard household cleansing agents excluding abrasive and concentrated (undiluted) products. Further maintenance is not necessary. |
The information contained in this web page is based upon our current knowledge and experience. As a wide range of potential influences may occur during the application and processing of our products, the processors of our goods are not released from the responsibility of carrying out their own tests. A legally binding document concerning the specific properties or the suitability for specific uses of any of our products may not be drawn up. The recipients of our products must abide by any industrial property rights as well as all existing laws and regulations. |