| TYPE: | Renoprop Super Clear | FINISH: | Smooth | | THICKNESS: | 2-12 mil (50 - 300 microns) | TOLERANCE: | ± 3% | | WIDTH: | 4-76 inches (101 - 1930 mm) | TOLERANCE: | ± 1 mm
(unless otherwise requested) | | SHRINKAGE: | 120°C
Time: 15 minutes | TOLERANCE: | MD: 1.5%
CD: 1.5% | | SPECIFIC GRAVITY: | .9 | | |
| PROPERTY | TYPICAL VALUE * | ASTM METHOD | | Tensile Strength MD/CD: | 6,000 psi | D-882 Method A | | % Elongation MD/CD | 1200% | D-882 Method A | | Tensile Modulus MD/CD: | 85,000 psi | D-882 Method A | | Weld Range (°C) | 142-161 °C | .25 sec, 1Kg min pull | | Gel Count: | <15 | Renolit Method | | Corona Treatment (if requested) | 38 dynes | D-2578 | | Gloss Specular (45°) | 86% | D-2457 | | Haze (air standard) | 9.1% | D-1003 | | Clarity | 50% | D-1746 | | * Typical values determined with 120m (4.7 mil) thick film. Typical values will vary with film thickness. |
Renoprop Super-Clear Film has been specifically designed for use with heat contact and impulse welding processes. It is suitable for stamping, perforation, folding, sheeting and sticking, and should be acclimatized before processing.Typical applications:
|
Typical applications:
- Office stationery/document products
Sheet protectors, photo album pages, document protectors - Archival storage products
Hobby and collector card multi-pocket pages, comic book sleeves, photo negative pages, coin holders - Disk/media cases
DVD & VHS over-wraps
To our knowledge the information contained herein is accurate. However, neither American RENOLIT Corporation nor any of its affiliates makes any warranty, expressed or implied, or accepts any liability in connection with this information or its use. This information is for use by technically skilled persons at their own discretion and risk and does not relate to the use of this product in combination with any other substance or any other process. This is not a license under any patent. The user alone must finally determine suitability of any information or material for any contemplated use, the manner of use and whether any patents are infringed. |