RENOPROP HIGH CLARITY POLYPROPYLENE
| TYPE: | Renoprop High Clarity | FINISH: | Smooth | | THICKNESS: | 2-12 mil (50 - 300 microns) | TOLERANCE: | ± 3% Local | | WIDTH: | 4-76 inches (101 - 1930 mm) | TOLERANCE: | ± 1 mm
(unless otherwise requested) | | SHRINKAGE: | 115-150 micron: 140°C
Time: 15 minutes | TOLERANCE: | MD: 1.5%
CD: 1.5% | | SPECIFIC GRAVITY: | .9 | | |
| PROPERTY | TYPICAL VALUE * | ASTM METHOD | | Tensile Strength | MD: >5000 psi | D-882 Method A | | | CD: >4500 psi | D-882 Method A | | % Elongation | MD: <1500% | D-882 Method A | | | CD: <1500% | D-882 Method A | | Tensile Modulus | MD: 60,000 psi | D-882 Method A | | | CD: 57,000 psi | D-882 Method A | | Coefficient of Friction: | <0.5 | D-1894 | | Weld Range: | 136 - 146°C | .25 sec, 1Kg min pull | | Cold Crack Resistance: | -10°C | D-1790 | | Gloss Specular (45°): | 88% | D-2457 | | Haze: | 9.7% | D-1003 | | Clarity: | 73% | D-1746 | | Gel Count: | <20 | SIF Test | | Corona Treatment (if requested) | ≥38 dynes/cm when shipped | D-2578 | | * Typical values determined with 120µ (4.7 mil) film. Typical values will vary with film thickness. |
Renoprop High Clarity Polypropylene Film has been specifically designed for use with heat contact and impulse welding processes. It is suitable for stamping, perforation, folding, sheeting and laminating, and should be acclimatized before processing.
Typical applications:
- Office stationery/document products
Sheet protectors, photo album pages, document protectors - Archival storage products
Hobby and collector card multi-pocket pages, comic book sleeves, photo negative pages, coin holders - Disk/media cases
DVD & VHS over-wraps - Miscellaneous applications
- Signage/banners (one- and two-side printable, indoor & outdoor)
To our knowledge the information contained herein is accurate. However, neither American RENOLIT Corporation nor any of its affiliates makes any warranty, expressed or implied, or accepts any liability in connection with this information or its use. This information is for use by technically skilled persons at their own discretion and risk and does not relate to the use of this product in combination with any other substance or any other process. This is not a license under any patent. The user alone must finally determine suitability of any information or material for any contemplated use, the manner of use and whether any patents are infringed. |